OPTIMIZATION OF PROTECTIVE COATINGS FOR ITEMS SPP METHOD OF MATHEMATICAL EXPERIMENT PLANNING
Abstract
The dependence of the two-component bidispersive filler content on physical, mechanical and thermal properties of epoxy composites to form a protective coating. The introduction of the optimal composition of the filler content provides improved coating properties. The мethod of mathematical planning of the experiment using orthogonal central composite plan defined the optimal content of aluminum oxide and boron crystal to form the crystalline surface layer of protective coating, which is: (Al2O3) - 60 parts; (BC) - 40 parts., 100 parts. epoxy oligomer ED-20 and 10 parts. hardener PEPA. Thus forming materials with improved properties: destructive stress in bending – σzh = 53,2 MPa, modulus of elasticity in bending – E = 8,0 GPa and heat (by Martens ) – T = 353 K.
References
Букетов А. В. Властивості модифікованих ультразвуком епоксипластів / А. В. Букетов, П. Д. Стухляк, І. В. Чихіра. – Тернопіль : Крок, 2011. – 201 с.
Прочность материалов и конструкций / Отв.ред. В. Т. Трощенко. – К. : Академпериодика, 2006. – 1076 с.
Оптимизация технологии нанесения покрытий по критериям прочности и износостойкости / [Б. А. Ляшенко, Е. К. Соловых, В. И. Мирненко, А. В. Рутковский, М. И. Черновол] ; под ред. В. В. Харченко – К. : Ин-т пробл. прочности им. Г.С.Писаренко НАН Украины, 2010. – 193 с.
Планирование эксперимента и применение вычислительной техники в процессе синтеза резины : сб. статей / под ред. В. Ф. Евстратова, А. Г. Шварца. – М. : Химия, 1970. – 352 с.
Зазимко В. Г. Оптимизация свойств строительных материалов : учебное пособие для вузов / В. Г. Зазимко – М. : Транспорт, 1981. – 103 с.